AMS SA-564 S17400 ( Precipitation-Hardening )

PDF Word Print
Grades | Stainless Steels | SA-564 S17400

  • AMS SA-564 S17400 Details

    AMS standard material SA-564 S17400 belongs to the USA, from the steel to the finished product, we have the perfect technology and many years of accumulation of experience, we can now produce products include steel coil, sheet, plate,round bar, square steel, steel wire, steel pipe, forgings, other...

    SA-564 S17400 Application:Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes

Chemical composition(mass fraction)(wt.%)
Elements Min.（≥） Max.（≤） Similar Remarks
C - 0.07
Mn - 1.00
Si - 1.00
P - 0.04
S - 0.03
Cr 15.50 17.50
Ni 3.00 5.00
Mo - -
Cu 3.00 5.00
Nb 0.15 0.45
Mechanical properties of grade SA-564 S17400
Yield
Rp0.2 (MPa)		 Tensile
Rm (MPa)		 Impact
KV (J)		 Elongation
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition HBW
618 (≥) 152 (≥) 33 31 12 Solution and Aging, Annealing, Ausaging, Q+T,etc 133
Physical properties of grade SA-564 S17400
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm
723 (≥) 477 (≥) 11 13 42 Solution and Aging, Annealing, Ausaging, Q+T,etc
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2		 - - -
422 687 647 - - -
SA-564 S17400 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED