Location » Home » Grades > Superalloys > B 670 N07718

ASTM B 670 N07718

PDF Word Print
Grades | Superalloys | B 670 N07718

  • ASTM B 670 N07718 Details

    ASTM standard material B 670 N07718 belongs to the USA, from the steel to the finished product, we have the perfect technology and many years of accumulation of experience, we can now produce products include steel coil, sheet, plate,round bar, square steel, steel wire, steel pipe, forgings, other...

    B 670 N07718 Application:Precipitation-Hardening Nickel Alloy (UNS N07718) Plate, Sheet, and Strip for High-Temperature Service

Chemical composition(mass fraction)(wt.%)
Elements Min.（≥） Max.（≤） Similar Remarks
C - 0.03
Cr 17.0 21.0
Mo 2.80 3.30
Ni 50.0 55.0
Al 0.20 0.60
Nb 4.75 5.50
Fe - Bal
Si - 0.35
Mn - 0.35
P - 0.015
S - 0.015
B - 0.006
Mechanical properties of grade B 670 N07718
Yield
Rp0.2 (MPa)		 Tensile
Rm (MPa)		 Impact
KV (J)		 Elongation
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition HBW
131 (≥) 333 (≥) 31 11 12 Solution and Aging, Annealing, Ausaging, Q+T,etc 313
Physical properties of grade B 670 N07718
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm
582 (≥) 478 (≥) 12 24 33 Solution and Aging, Annealing, Ausaging, Q+T,etc
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2		 - - -
358 766 444 - - -
B 670 N07718 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED